As example we may point out the natural pozzolans of volcanic origin, which are originated by magma explosive eruptions, which easily get cold thus turning into a micro-porous glass, mainly containing SiO2, Al2O3 y Fe2O3 Massazza, 1993When adding such materials to the cement paste, they react with the CaOH2released during its hydration process forming calcium silicates H-C-S of stable, hydraulic and non-soluble phases Rosell-Lam, Villar-Cociña, & Frías, 2011, thus providing different benefits from different points of view, such as mechanical, durability and reduction of heat release in cementious elements Alp et al., 2009; J. L. Costafreda, Calvo, & Parra, 2011; Hossain & Lachemi, 2007, 2010; Hossain, 2005, 2006; Kaid, Cyr, Julien, & Khelafi, 2009; Ramezanianpour, Samadian, & Mahdikhani, 2012; Siad, Mesbah, Kamali, Khelafi, & Moulli, 2010.
Un ejemplo de esto son las puzolanas naturales de origen volcánico que son el resultado de la explosión del magma que se enfría rápidamente para formar un vidrio microporoso constituido principalmente por SiO2, Al2O3 y Fe2O3 Massazza, 1993. Al incorporar estos materiales al cemento, reaccionan con el CaOH2 liberado durante la hidratación del mismo y forman silicatos cálcicos hidratados C-S-H fases estables, hidráulicas e insolubles Rosell-Lam, Villar-Cociña, & Frías, 2011 que confieren diversos beneficios desde el punto mecánico, de durabilidad y reducción en la liberación de calor en los elementos cementicios Alp et al., 2009; J. L. Costafreda, Calvo, & Parra, 2011; Hossain & Lachemi, 2007, 2010; Hossain, 2005; Kaid, Cyr, Julien, & Khelafi, 2009; Ramezanianpour, Samadian, & Mahdikhani, 2012; Siad, Mesbah, Kamali, Khelafi, & Moulli, 2010.