Then CPE and resistivity are found associated to the first elements in concrete external zone. Such elements can be originated by generated reactions or by surface absorption of some species introducing CO2, and then from intermediate frequencies it is possible to find elements such as CPE and resistivity, such elements are associated to paste/aggregates interfacial transition zone in concrete. In low frequency domain the load transference process is normally found, in combination with mass transference process, which correspond to the last R and CPE, such elements are placed in the interfacial transference zone corresponding to concrete and steel.
El circuito de la Figura 7 muestra una primera resistencia Rc+s asociada a la solución de poro del concreto, esta es hallada a altas frecuencias a 100kHz; luego encontramos un CPE y una resistencia asociada a la primeros elementos que se encuentran en el concreto en su parte externa, estos elementos pueden ser debidos a las reacciones generadas o absorción superficial de algunas de las especies con el ingreso del CO2; luego a frecuencias intermedias podemos encontrar otros elementos tales como un CPE y una resistencia, estos elementos están asociados a la zona de transición interfacial pasta - agregados que constituyen el concreto; en dominio de bajas frecuencias normalmente se encuentra el proceso de transferencia de carga en combinación con el proceso de transferencia de masa, esto corresponde a la última R y al CPE, estos elementos están ubicados en la zona interfacial correspondiente al concreto y el acero.