The frictional stress value for the steel being studied was very high, H0 = 1.413 GPa, considering the H0 = 0.096 GPa determined by Petch 1953 on interstitial free pure iron studding having grain sizes from 20 to 100 microns.
El valor de la resistencia de fricción para el acero estudiado H0 = 1.413 GPa es muy alto si se considera el H0 = 0.096 GPa determinado por Petch 1953 sobre hierro puro libre de intersticiales cubriendo tamaños de grano desde 20 µm a 100 µm.