Merlati & al mention the emergence of pinkish pigmentation in the root and crown of amalgam-filled teeth and subjected to 1,000°C and 1,100°C, whereas Moreno & al describe the presence of the aforementioned pigmentations in enamel located around the amalgam filling when subject to temperatures from 600°C up to 1,200°C. Reddish-brownish pigmentations are associated to the oxidation caused by high temperatures sustained by copper at temperatures from 450°C onwards. The brownish-golden halo which surrounds the amalgam obturation at temperatures between 800°C and 1,200°C is associated to mercury vapors, to copper itself and to silver oxides.
Merlati et al. hicieron referencia a la aparición de pigmentos rosados en la raíz y en la corona de los dientes obturados con amalgama y sometidos a 1,000 y 1,100 °C, mientras que Moreno et al. reportaron dichos pigmentos en el esmalte alrededor de la amalgama entre los 600 y 1,200 °C. Los pigmentos rojizos-pardo se asocian con la oxidación por altas temperaturas que sufría el cobre a partir de los 450 °C, el halo dorado-marrón que circunscribe la obturación en amalgama entre los 800 °C y los 1,200 °C se asocia a los vapores de mercurio, al mismo cobre y a los óxidos de plata.