The strain tensor of matrixe was equal to the strain tensor of composite material e . The normal strain e obtained from axial behavior of the bars in r direction was equal to the normal term of composite material strain tensor err . The normal strain e obtained from the axial behavior of the bars in s direction was equal to normal term ess in s direction of the composite material strain tensor. Given that the bars crossing a crack had shear capacity, it was assumed that the engineering shear strain g of the bars was equal to term grs in the rs plane of the composite material strain tensor.
La compatibilidad entre el tensor de deformaciones del material compuesto y las deformaciones de cada material componente está definida mediante las siguientes hipótesis: 1 el tensor de deformaciones en la matriz ees igual al tensor de deformaciones del material compuesto e, 2 la deformación longitudinal eresultante del comportamiento axial de las barras en dirección r es igual a la componente longitudinal en dirección r del tensor de deformaciones del material compuesto err, 3 la deformación longitudinal eresultante del comportamiento axial de las barras en dirección s es igual a la componente longitudinal en dirección s del tensor de deformaciones del material compuesto ess, y 4 dada la capacidad a cortante de las barras cuando cruzan una fisura, se puede suponer que la deformación angular ingenieril de las barras ges igual a la componente de deformación angular ingenieril del material compuesto en el plano rs indicada como grs.