This equivalent circuit was applicable for coatings exposed to a 3.5%wtNaClsolution Rs represented electrolyte resistance in the case of the coatings of interest, Cc was coating layer capacitance and Rpo was resistance at the solution-coating interface in paint -based systems, referring to the coating formed by the Alodine 5700system, epoxy primer and paint finish, and in the case of synthetic resin AH1-based systems, it concerned the system consisting of Alodine 5700, antacid Hetron197 primer and resin-3.Increased Ccwas a direct relationship between the level of coating degradation while a decrease in Rpon was related to increased water absorption or permeability.
Este circuito equivalente es aplicable para los recubrimientos expuesto a una solución de NaCl 3,5 wt.%. El parámetro de Rs representa la resistencia del electrolito en el caso de los recubrimientos de interés; Cc es la capacitancia de la capa del recubrimiento y Rpo es la resistencia en la interfase soluciónrecubrimiento; en el caso de los sistemas base pintura, hace referencia al recubrimiento conformado por el sistema Alodine 5700, primer epóxico y pintura de acabado, y en el caso de los sistemas base resinas sintéticas AH1 se refiere al sistema conformado por Alodine 5700, imprimante y resina antiácida Hetron197-3, donde el incremento en Cc es una relación directa del nivel de degradación del recubrimiento, mientras que la disminución en Rpo se encuentra relacionada con el incremento en absorción de agua o permeabilidad.